JIS G3114 hot-rolled plate for welded structure S355JR, which one has higher tensile strength?

Hull structural steel is divided into general thickness and high-strength steel. General strength steel is divided into four grades of A, B, C and D; high-strength steel is divided into two strength grades and three quality grades; AH32, DH32, EH32, AH36, DH36, JIS G3114 hot-rolled plate for welded structure, EH36. In order to ensure quality and ensure sufficient toughness of hull structural steel, the chemical composition of Mn / C is required to be above 2.5, and the carbon equivalent is also strictly required. Our Hull structural steel plates can be supplied with certificates from different classification societies.

The chemical composition difference between JIS G3114 hot-rolled plate for welded structure, Q235B and 20# steel is as follows:
The chemical composition of 20# steel: C: 0.17-0.23%, Si: 0.17-0.37%, Mn: 0.35-0.65%, Cr: ≤ 0.25%, Ni: ≤ 0.30%, Cu: ≤ 0.25%. Chemical composition of Q235B steel: C: ≤ 0.20%, Si: ≤ 0.35%, Mn: ≤ 1.40%, P: ≤ 0.045%, S: ≤ 0.045%.
The difference of mechanical properties between JIS G3114 hot-rolled plate for welded structure, Q235B and 20# steel is as follows:
The mechanical properties of 20# steel: tensile strength 410 MPa; yield strength 245 MPa; elongation after fracture: 25; reduction of area: 55; no impact. Q235B steel mechanical properties: tensile strength 370-500 Mpa; yield strength: ≥ 235 Mpa; elongation after fracture: 25; impact absorption energy: 27J.

If customers have any difficult problems during use of the steel materials, they can contact the company's after-sales service department to feedback the existing problems. The after-sales department will reply as soon as possible to ensure that each customer has a good after-sales experience. Under special circumstances, the after-sales service department will start the problem-solving process, and the engineers in charge of the area will quickly follow up to solve the problem.