What Are The Mild Steel Plate SPA-H rusty steel for sculpture Properties

Zhengzhou BBN steel company was established in 2000. After more than ten years of development, it has formed a professional operation pattern integrating R&D, production, sales and after-sales service. In recent years, SPA-H rusty steel for sculpture based on a high starting point and high technology, the company has vigorously developed various steel products SPA-H rusty steel for sculpture and deep-processed parts, steel structures, precision castings, seamless pipes.

Grades SPA-H rusty steel for sculpture, Q345 (16Mn) and Q390 steel have good comprehensive mechanical properties, good welding performance, cold and hot workability and corrosion resistance. C, D, E grade steel has good low temperature toughness. Mainly used for ships, boilers, pressure vessels, petroleum storage tanks, bridges, power station equipment, lifting and transportation machinery and other higher-load welding structural parts.

A514 grade S high strength structural steel chemical composition (melting analysis)%
C: 0.11-0.21, Si: 0.15-0.45, Mn: 1.10-1.50, P max.: 0.035, S max.: 0.035, B max.: 0.005, Mo: 0.10-0.60, V max.: 0.06.
The mechanical properties in thickness (mm) T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

It is very important for a company to have a sound after-sales service system, which better guarantees the interests of customers and increases the reliability of the company's products in the hearts of customers. Our company has a dedicated after-sales service team and good after-sales service reputation, and has been recognized by customers over the past decades. Whenever there is problem about our SPA-H rusty steel for sculpture steel materials during application on the user site, our after-sales service persons will assist to find solutions at the first time.