SPA-H weathering steel equivalent GB standard material

home > News

SPA-H weathering steel equivalent GB standard material

It is very important for an enterprise to have a sound after-sales service system, which not only ensures the normal outflow and inflow of the company's products, but also improves the trust of the company's products in the hearts of customers. Our company has a special after-sales service team and good after-sales service reputation. In case of any problem in the use of our steel products SPA-H weathering steel , whether quality problem or not, the after-sales service department will assist in solving the problem as soon as possible, and regularly consult and track the use of the steel products.

S45C steel plate chemical composition: C 0.42~0.48, Si 0.15~0.35, Mn 0.60~0.90, P≤0.030, S≤0.035, Cu≤0.30, Ni≤0.20, Cr≤0.20
Mechanical properties of SPA-H weathering steel product
Tensile strength>686MPa
Yield strength>490MPa
Elongation δ5>17%
Shrinkage ψ>45%
Impact toughness value>78J/cm2
The hardness is 201~269HB.

The main applications of normalizing are as follows:① For low carbon steel, SPA-H weathering steel. The hardness of low carbon steel after normalizing is slightly higher than that after annealing, and the toughness is also better, so normalizing can be used as the pretreatment of cutting.② For medium carbon steel, normalizing can be used as the final heat treatment instead of quenching and tempering treatment, or as the preparation treatment before surface quenching by induction heating.③ Normalizing can be used in tool steel, bearing steel, carburizing steel and so on, which can eliminate or inhibit the formation of network carbide, thus obtaining the good microstructure needed for spheroidizing annealing.④ Normalizing can refine the cast structure and improve the machinability of steel castings.

As to the Chemical composition, the different content is a main on carbon content, while the carbon content of SPA-H weathering steel, A283Gr. D is no more than 0.27% and it is higher than Grade C (≤0.24%) ; as to the mechanical property, the differences are tensile strength and yield strength, while the tensile strength of ASTM A283 Gr.D is 415-550MPa (60-80 ksi) and yield strength of ASTM A283 Grade D is 230MPa (33 ksi).

The predecessor of Ningbo port is Ningbo Port Authority. Ningbo port consists of Beilun port, Zhenhai port, Ningbo port, Daxie port and Chuanshan port. It is a multi-functional and comprehensive modern deep-water port integrating inland river port, estuary port and seaport.

The company specializes in hot rolled plates producing, steel plate processing, steel plates cutting, carbon steel plate weldding and exporting of wide and thick steel plates. BBN company has high-quality CNC SPA-H weathering steel steel plate cutting processing equipment, professional technical personnel, and supporting marketing and after-sales service system. Sincerely welcome new and old customers to visit our company, BBBN company will always be your reliable choice.