How to choose hot rolled SPA-H beam steel corten plate supplier

BBN steel company was founded in 2000, starting the international business in 2010 and successfully being approved and certified by ISO9001:2008. After ten years development, BBN steel has become the large-scale comprehensive enterprise group, combining steel trading, SPA-H beam steel corten plate plate processing, and steel distribution, also have large warehouse and processional representatives both inTianJin, Zhengzhou and Beijing city.

SPA-H beam steel corten plate, Wear resistant steel plate has good wear resistance:
The chemical composition of the alloy wear-resistant layer is 4-5% carbon and 25-30% chromium. The volume fraction of Cr7C3 carbide in the metallographic structure is more than 50%. The macro hardness is HRC56-62 and the hardness of chromium carbide is HV1400-1800. Because the carbides are distributed perpendicularly in the direction of wear, even when compared with cast alloys of the same composition and hardness, the wear resistance is more than doubled.

A514 grade R high strength structural steel chemical composition (melting analysis)%
C: 0.15-0.20, Si: 0.20-0.35, Mn: 0.85-1.15, P max.: 0.035, S max.: 0.035, B max.: 0.005, Cr: 0.40-0.65, Ni: 0.90-1.10, Mo: 0.15-0.25, V: 0.03-0.08
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

The company attaches great importance to the cultivation of team spirit. Personal strength is weak. After sales service departments, leaders and subordinates often communicate with each other. Everyone often holds meetings to discuss their problems in after-sales service, discuss technical difficulties, discuss how to improve work efficiency, how to better deal with user complaints, etc.