Chemical elements of Q345NQR2 tempered steel

Our company can produce Q345NQR2 tempered steel, EN10025-2 S355J2 structural steel plates and sheets up to 400mm thickness. S355J2 steel consists of S ( for structural steel), 355 (indicates the minimum specified yield strength value in MPa for thickness less than 16mm), J2( for a minimum impact energy value of 27J at -20ºC). EN S355J2 structural steel plates are suitable for cold flanging, delivery condition normalized rolled or as rolled.We are a professional Q345NQR2 tempered steel steel raw material supplier with a history of 17 years. After years of development, the company's steel plates and coils are widely used in construction, machinery manufacturing, container manufacturing, shipbuilding, bridge construction and other fields around the world. With good product Q345NQR2 tempered steel quality, we have solid project cooperation with foreign governments or leading enterprises such as Egypt, Bangladesh, Myanmar, Thailand, Philippines, Vietnam, Venezuela, Peru, Mexico, the United States, Portugal, Russia, Iran, Iraq, Pakistan, etc.Non-destructive flaw detection of steel plates is a test method for inspecting the Q345NQR2 tempered steel surface and internal quality of the inspected parts without damaging the working state of the workpiece or raw materials. Commonly used Q345NQR2 tempered steel steel plate flaw detection methods include: X-ray flaw detection, ultrasonic flaw detection, magnetic particle flaw detection, penetration flaw detection, eddy current flaw detection, gamma-ray flaw detection, fluorescent flaw detection, color flaw detection and other methods. Physical flaw detection is non-destructive flaw detection without any chemical changes.Between alloy wear-resistant layer and the substrate of wear-resistant steel is metallurgically bonded. Through special equipment and automatic welding process, high-hardness self-shielding alloy welding wire is uniformly welded on the substrate, and the number of composite layers is one to two or even multiple layers. During the compounding process, due to the different alloy shrinkage ratio, uniform transverse cracks occur. It is a distinctive feature of wear-resistant steel plates, Q345NQR2 tempered steel.The after-sale service of iron and steel products includes after-sale tracking service, technical guidance, transfer of relevant bills, handling of objections and many other contents. The handling of quality objections accounts for a large proportion. When dealing with these problems, we should distinguish the responsibilities, and compensate or return the inconvenience or loss caused to users due to steel.