What are the equivalent steel grades of A588 Grade A hot-rolled angle steel?

The A588 Grade A hot-rolled angle steel plate products have passed the EU CE certification, and have been recognized by China, France, the United States, the United Kingdom, Germany, Italy, Japan, South Korea and other eight classification societies for high-strength ship plates. The steel strand products have passed the United States (PTI) certification. The A588 Grade A hot-rolled angle steel products enjoy a high reputation in the domestic and foreign markets. The products are applied to national key projects and sold to 37 countries and regions such as EU, Middle East, Southeast Asia and America.

The difference between low alloy high strength steel plate and carbon steel plate, A588 Grade A hot-rolled angle steel:(1) Strength difference between low alloy high strength steel plate and carbon steel plate:The strength of low alloy high strength steel plate is higher than that of carbon steel plate;(2) Hardness difference between low alloy high strength steel plate and carbon steel plate:The hardness of low alloy high strength steel plate is higher than that of carbon steel plate;(3) Usage difference between low alloy high strength steel plate and carbon steel plate:The application range of low alloy high strength steel plate is wider than that of carbon steel plate.

Corrosion resistant steel plate, as a new generation of advanced steel material, has 2-5 times of atmospheric corrosion resistance as ordinary carbon steel such as A588 Grade A hot-rolled angle steel, and the longer the service time, the more prominent the corrosion resistance. Due to its characteristics of rust resistance, coating free, thinning and consumption reduction, labor saving and energy saving, corrosion resistant steel plate can be applied to steel structures exposed to the atmosphere for a long time, such as buildings, vehicles, bridges, towers, etc., and can also be used to manufacture structural parts such as containers, railway vehicles, oil derricks, seaport buildings, oil production platforms, etc.

Heat treatment is a very important process to improve the performance of A588 Grade A hot-rolled angle steel etc. metal materials. The process of heating, heat preservation and cooling the steel in solid state to obtain the required structure and properties.

Chemical composition of A588 Grade A hot-rolled angle steel, Q345D steel plate: C: ≤0.18; Si: ≤0.50; Mn: ≤1.70; P: ≤0.030; S: ≤0.025; Nb: ≤0.07; V: ≤0.15; Ti: ≤0.20; Cr: ≤0.30; Ni: ≤0.50; Cu: ≤0.30; N: ≤0.012; Mo: ≤0.10; Als: ≥0.015. Yield strength (MPa) of Q345D steel plate: ≤16mm: ≥345; 16-40mm: ≥335; 40-63mm: ≥325; 63-80mm: ≥315; 80-100mm: ≥305; 100-150mm: ≥285; 150-200mm: ≥275; 200-250: ≥275; 250-400: ≥265. Tensile strength of Q345D low alloy steel: 450-630(MPa). Elongation: ≥21. Impact test: -20 ℃: ≥34.

The alloy steel plate is among our business scope, and it is one of our main product. If you have any demands or questions about alloy steel plate, such as 34CrMo4 A588 Grade A hot-rolled angle steel material properties, 42CrMo4 AISI equivalent, 12Cr1MoV equivalent ASTM, 40Cr material specification, 42CrMo hardness, 50CrMo4 chemical composition and so on, please free free to communicate with us. We have professional technical team and sales team, who will give you A588 Grade A hot-rolled angle steel professional answers and quotation about alloy steel plate in time.

Both parties shall confirm the A588 Grade A hot-rolled angle steel material object and the quality of the products, confirm the reasons for the defects and the quality of the products, and sign the quality inspection agreement. Major quality objections shall be reported to relevant leaders in a timely manner, and shall be discussed and solved with the A588 Grade A hot-rolled angle steel steel plant.