Do you want any logistics service, then call us: +86-371-86151827
The company's operation is based on the principle of "quality for survival, reputation for development". In terms of management, we adhere to the principle of people-oriented, service-oriented and customer-oriented. All staff of the company have the courage to open up, unite and forge ahead, and work hard to grasp the good situation of global economic development, actively strengthen communication with outstanding enterprises in the A588GrC strip manufacturer industry, keep pace with the times, and move towards a new course!
A588GrC strip manufacturer surface cracks refer to the linear cracks on the surface of A588GrC strip manufacturer, which should generally be the same as the forging or rolling direction. Formation reason: it is mainly due to the hairline, hot crack and cold crack caused by surface over burning, decarburization, looseness, deformation and excessive internal stress during processing (forging, rolling, heat treatment, quenching and tempering), as well as the high content of sulfur and phosphorus impurities on the surface. Inspection method: A588GrC strip manufacturer surface cracks can be detected by naked eye observation, acid pickling, magnetic particle inspection, coloring inspection and metallographic method.
Good weldabilityBecause of its low carbon content, low alloy element content, good plasticity and low hardenability, this material A588GrC strip manufacturer is not suitable to have quenching structure or crack at the weld. The cold and hot pressure processing performance is good. Because of its good plasticity and small deformation resistance, it is not easy to produce cracks after pressure processing. Good corrosion resistanceUnder various atmospheric conditions, it has higher corrosion resistance than carbon steel.
Its weatherability is the protection of the oxide layer of weatherproof steel. The mechanism of corrosion resistance of weathering steel is mainly based on the analysis of long-term exposed rust layer. Generally speaking, it is believed that weathering steel can form a dense layer of weathering rust through long-term exposure, which has a good protective effect on weathering steel, A588GrC strip manufacturer.
ASTM A537 class 1 boiler plate is pressure vessel steel. A588GrC strip manufacturer, A537 class 1 boiler plate chemical elements include C, Si, Mn, P, S, Mo, Ni, etc. Among them, the carbon content is 0.24 max., Si content is 0.13-0.55%, Mn content is 0.92-1.72%, the max. contents for both P and S are 0.035%, the Mo content is 0.09% max, and the Ni content is 0.38% max. A537 class 1 boiler plate properties: A537 class 1 boiler plate tensile strength is 450-585 MPa, min. yield strength is 310 MPa, and min. elongation in 2 in.(50mm) is 18%.
For ASTM A573 Grade 70/A573 Gr.70 carbon manganese silicon steel plates, our company would issue the original mill test certificate A588GrC strip manufacturer EN 10204 3.1 for clients when arrange delivery, so that clients can trace the A573 Gr.70 plates origin easily.
The company strengthens process management and pays attention to assessment. One of the key points of good service is to strengthen the process management and improve the evaluation mechanism. Make the after-sales service system more perfect and provide better service for customers.
Ask for the instant quotation