Our company will set up a full-time service engineer for the project, who is responsible for the interface and coordination of technical support and after-sales service of the SPA-C material project. In response process of customer service center, in case of technical support and after-sales service demand, the user shall contact the full-time engineer of SPA-C material customer service center, and the technical personnel will give corresponding answers and on-site treatment according to the needs of users.

Wear-resistant plates are very easy to understand from the literal. They are steel plates designed for large-area wear conditions. Because of its outstanding wear resistance, wear plates have their own unique uses, such as mining machinery and equipment. Ore processing, transportation of ore, ore and equipment often produce severe friction. SPA-C material, General steel plates cannot be subjected to friction for a long time and are easily damaged. Wear plates are very effective in solving this problem.

asme sa514 gr F structural quality steel chemical composition%
C: 0.10-0.20, Si: 0.15-0.35, Mn: 0.60-1.00, P max.: 0.035, S max.: 0.035, Ni: 0.70-1.00, Cr: 0.40-0.65, Mo: 0.15-0.25, V: 0.03-0.08, Cu: 0.15-0.50, B: 0.001-0.005
The mechanical properties in the plate thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

Both parties shall confirm the SPA-C material material object and the quality of the products, confirm the reasons for the defects and the quality of the products, and sign the quality inspection agreement. Major quality objections shall be reported to relevant leaders in a timely manner, and shall be discussed and solved with the SPA-C material steel plant.